Auropent® AH
|
| WAK-Factor - 25-500 °C 10-6K-1 |
14,0 |
| WAK-Factor - 25-600 °C 10-6K-1 |
14,3 |
| Density - g/cm3 |
18,9 |
| Melting interval - °C |
1080 - 1150 |
| Preheating temperature - °C |
850 |
| Casting temperature - °C |
1315 |
| Vickers hardness - HV5/30 |
(selfhardening) |
220 |
| Vickers hardness - HV5/30 |
(after the burning) |
220 |
| Vickers hardness - HV5/30 |
(hardened) |
240 |
| Expansion limit - N/mm2 |
(selfhardening) |
420 |
| Expansion limit - N/mm2 |
(hardened) |
600 |
| Break expansion - A % |
(selfhardening) |
5 |
| Break expansion - A % |
(hardened) |
2 |
| Oxidation - °C/10 min |
960 |
| E-Modul - kN/mm2 |
93 |
|
Auropent® B
|
| Density - g/cm3 |
16,8 |
| Melting interval- °C |
890 - 970 |
| Preheating temperature - °C |
700 |
| Casting temperature - °C |
1120 |
| Vickers hardness - HV5/30 |
(selfhardening) |
180 |
| Vickers hardness - HV5/30 |
(hardened) |
200 |
| Expansion limit - N/mm2 |
(selfhardening) |
180 |
| Expansion limit - N/mm2 |
(hardened) |
320 |
| Break expansion - A % |
(selfhardening) |
27 |
| Break expansion - A % |
(hardened) |
13 |
| E-Modul - kN/mm2 |
93 |
|
Auropent® A
|
| WAK-Factor - 25-500 °C 10-6K-1 |
14,5 |
| WAK-Factor - 25-600 °C 10-6K-1 |
14,8 |
| Density - g/cm3 |
18,9 |
| Melting interval - °C |
1035 - 1110 |
| Preheating temperature - °C |
850 |
| Casting temperatur - °C |
1270 |
| Vickers hardness - HV5/30 |
(selfhardening) |
180 |
| Vickers hardness - HV5/30 |
(after the burning) |
190 |
| Vicker hardness - HV5/30 |
(hardened) |
200 |
| Expansion limit - N/mm2 |
(selfhardening) |
260 |
| Expansion limit - N/mm2 |
(hardened) |
300 |
| Break expansion - A % |
(after the burning) |
10 |
| Break expansion - A % |
(hardened) |
7 |
| Oxidation - °C/10 min |
960 |
| E-Modul - kN/mm2 |
93 |
|
Auropent® I
|
| Density - g/cm3 |
18,9 |
| Melting interval - °C |
910 - 980 |
| Preheating temperature - °C |
650 |
| Casting temperatur - °C |
1100 |
| Vickers hardness - HV5/30 |
(selfhardening) |
110 |
| Vickers hardness - HV5/30 |
(hardened) |
130 |
| Expansion limit - N/mm2 |
(selfhardening) |
200 |
| Break expansion - A % |
(selfhardening) |
50 |
| E-Modul - kN/mm2 |
93 |
Auropent®
KFO - Wires
KFO wires for: • Bionator
• Crozant
Before the bending, the wire must be softened at 750 C for
5 minutes, afterwards chilled in water.
After the bending and before polymerication the wire must
be tempered at 500 C for 15 minutes.
|
|
|